改性ZSM-5分子筛催化合成乙酸戊酯

来源 :光谱实验室 | 被引量 : 0次 | 上传用户:mir_lww0
下载到本地 , 更方便阅读
声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架
论文部分内容阅读
以ZSM-5为原料,采用浸渍法将其交换成HZSM-5,以HZSM-5为催化剂,对以冰乙酸和正戊醇为原料合成乙酸戊酯的反应条件进行了研究。研究表明,以1.0m ol/L硫酸浸渍后的ZSM-5催化活性最高,当醇酸摩尔比为1.1∶1,催化剂用量为0.4g,反应时间为90m in,反应温度为125—135℃,酯化率可达82.5%。 ZSM-5 was used as raw material, and HZSM-5 was exchanged by impregnation method. The reaction conditions of synthesizing amyl acetate from glacial acetic acid and n-amyl alcohol were studied by using HZSM-5 as catalyst. The results showed that ZSM-5 had the highest catalytic activity after impregnated with 1.0 mol / L sulfuric acid. When the molar ratio of alkyd was 1.1: 1, the amount of catalyst was 0.4 g, the reaction time was 90 min, the reaction temperature was 125-135 ℃, Esterification rate up to 82.5%.
其他文献
通过车削试验、浸泡试验和极化曲线的测定,研究了氮对耐蚀塑料模具钢切削性能和耐腐蚀性能的影响,并与4Cr13钢作了比较.研究结果表明含氮SW333钢的切削性能和耐蚀性均优于4Cr
以Fe3O4粒子和3-氨丙基三乙氧基硅烷(APTES)为原料制备了有机硅表面修饰的磁性复合物,通过透射电镜(TEM)、热重分析(TGA)、X射线衍射(XRD)、红外光谱(FT-IR)等对其形貌和组成
采用十八烷基硅烷键合硅胶为固定相,以乙腈-甲醇-0.5%醋酸铵溶液(67∶12∶21)为流动相,检测波长为210nm。齐墩果酸在0.0195—0.78μg范围内线性关系良好(r=0.9997),回收率为9
以牡丹皮为原料研究了丹皮酚的提取工艺,并对丹皮酚的荧光光谱性质进行了研究,探讨了酸碱对丹皮酚荧光性质的影响。研究结果表明,随着丹皮酚浓度的增加荧光强度逐渐减弱;在酸
给出了一种有向图的定义.得到了这种有向图从始点到其它任一顶点之间最长路的算法.在不影响整个最长路的条件下,通过边上机动资源变化的分析,给出了这种有向图灵敏度分析的方
对碳纤维与树脂界面上发生的铺展作用进行了详细研究。分析了时间和温度对树脂在涂层表面铺展作用的影响。结果表明:升高温度有利于铺展行为的发生,且温度升到70℃以上时铺展
在循环流化床冷态试验台上,开展了J阀结构参数对于回料量影响的试验研究。试验表明,在相同回料风量下,J阀循环室高度降低,有利于提高回料量,循环室与支持室通道高度在一定范
探讨夏桑菊提取的最佳工艺条件,并比较提取物在不同提取剂中对羟自由基的清除作用。结果表明夏桑菊提取物除石油醚层外,对羟自由基都有一定的清除作用,其中乙酸乙酯提取物清
光声光谱检测可很好地应用在植物光合作用的研究领域,可更有效于传统检测方法并已在大量检测研究中得以证明.在一套光声光谱仪检测装置中,光声池是其核心部件,其设计好坏直接