High power laser cladding of [(Fe0.5Co0.5)0.75B0.2Si0.05] 95.7 Nb4.3 powder mixture afier-remelting was performed to fabricate Fe-based metallic glass coating o
【机 构】
：
Shanghai Key Laboratory of Materials Laser Processing and Modification
论文部分内容阅读
High power laser cladding of [(Fe0.5Co0.5)0.75B0.2Si0.05] 95.7 Nb4.3 powder mixture afier-remelting was performed to fabricate Fe-based metallic glass coating on the surface of steel of China Classification Society:Grade B (CCS-B).Scanning electron microscopy (SEM),X-ray diffraction (XRD),transmission electron microscopy (TEM)with energy dispersive spectrometer (EDS),Vickers hardness tester and corrosion resistance tester were employed to characterize microstructures and evaluate properties of this coating.According to the results of SEM ,XRD and TEM ,the cladding coating consisted of nanocrystalline embedded in amorphous phase.EDS data indicated that Nb segregated in the amorphous matrix.The results of hardness test revealed that the hardness of the top layer was higher than that of the inner layer of the coating.The coating exhibited excellent corrosion resistance in a 3.5% NaCl solution.
其他文献
根据禾谷镰孢菌参考菌株NRRL31084(PH-1)的γ-微管蛋白基因核苷酸序列设计5对引物,采用PCR方法从禾谷镰孢菌(Fusarium graminearum)对多菌灵(MBC)的敏感菌株、室内诱导及田间
采用高密点阵技术从黄鳝雄性性腺cDNA文库中获得8个克隆,序列分析和BLAST结果显示它们编码的蛋白质分别与40S核糖体蛋白S4,S9,S16,S17,S20和60S核糖体蛋白L7,L18a,L29高度同
将健康的围产期奶牛30头随机分为3组,每组10头.其中Ⅱ组为对照组,Ⅰ组和Ⅲ组分别为试验组.Ⅰ、Ⅱ、Ⅲ组均于产前28 d开始分别饲喂NRC标准减少20%日粮(能量摄入80%组)、NRC标
研究了蛇鲻(Saurida wanieso)冰藏和冻藏过程中K值、挥发性盐基氮(TVBN)、Mf Ca2+-ATPase全活性等鲜度指标的变化,并研究了高压加工法制备对蛇鲻鱼糕凝胶形成能的影响.结果表
1999年和2002年在田间条件下,对水稻群体光合速率及稻米碾磨和外观品质进行了研究.结果表明,不同水稻品种群体光合速率和稻米品质各指标存在差异,齐穗后15天左右的群体光合速
于2002-2003年度采用4个不同基因型小麦品种豫麦18号、豫麦49号、百泉41和郑引1号,研究了播期对面粉粉质参数及淀粉糊化特性的影响。结果表明,小麦基因型和播期对品质性状均
目的:探讨真菌诱导的豚鼠变应性鼻炎鼻黏膜中Eotaxin基因的表达及其意义.方法:采用真菌互隔交链孢霉致敏豚鼠建立变应性鼻炎动物模型,用组织病理学方法观察鼻黏膜改变,原位杂
目的:探讨细菌脂多糖(LPS)诱导离体鼻黏膜上皮细胞致炎后p38MAPK的活性变化及意义。方法:采用无血清原代培养法行正常鼻黏膜上皮细胞分离和培养,采用不同时间、不同浓度的LPS
Multi-hop relay is a significant topic in the wireless communication and it is provisioned in the 802. 16j standards. At present, the major research on multi-ho