The deformation behaviour and the nature of dislocations of the Al3Ti-base L12 alloya modified with Fe and Mn etc, were investigated. The results show that the deformation and fracture character istics are closely related to the alloy compositions. The effect of hot-working process on the room tem perature ductility is remarkable, not only resulting in an appreciable improvement of compressive properties but also showing a 0.28% plastic strain in tensile test. The SISF dissociation of a < 110>dislocations on {111} planes was found at room temperature. The determined dissociation scheme is consistent with the mechanical behaviour of these alloys in the lower temperature region.
The deformation behavior and the nature of dislocations of the Al3Ti-base L12 alloya modified with Fe and Mn etc, were investigated. The results show that the deformation and fracture character istics are closely related to the alloy compositions. The effect of hot-working process on the room tem perature ductility is remarkable, not only in an appreciable improvement of compressive properties but also showing 0.28% plastic strain in tensile test. The SISF dissociation of a <110> dislocations on {111} planes was found at room temperature . The determined dissociation scheme is consistent with the mechanical behavior of these alloys in the lower temperature region.