A sandwich structure with cladding alloyed 316L stainless steel on plain carbon steel was prepared by means of powder metallurgy (PM) processing. Electrolytic Cu and prealloyed bronze (95Cu wt pct, 5Sn wt pct) were added in different contents up to 15% into the surface cladded 316L layers and the effect of alloying concentrations on the corrosion resistance of the 316L cladding layers was studied. The corrosion performances of the cladding samples were studied by immersion tests and potentio-dynamic anodic polarization tests in H_2S0_4 and FeCl_3 solutions. Both 316L and alloyed 316L surface layers with 1.0 mm depth produced by PM cladding had an effect to improve corrosion resistance in H2SO4 and FeCI3 solutions. Small Cu and bronze addition (4%) had a positive effect in H_2SO_4 and FeCl3 solutions. 4% Cu alloyed 316L surface layer produced by PM cladding showed similar anodic polarization behaviour to the 316L cladding layer in H_2SO_4 and FeCl_3 solutions. A sandwich structure with cladding alloyed 316L stainless steel on plain carbon steel was prepared by means of powder metallurgy (PM) processing. Electrolytic Cu and prealloyed bronze (95Cu wt pct, 5Sn wt pct) were added in different contents up to 15% into the Surface cladded 316L layers and the effect of alloying concentrations on the corrosion resistance of the 316L cladding layers was studied. The corrosion performances of the cladding samples were studied by immersion tests and potentio-dynamic anodic polarization tests in H_2S0_4 and FeCl_3 solutions. Both 316L and 4% Cu alloyed 316L surface with 1.0 mm depth produced by PM cladding had an effect to improve corrosion resistance in H2SO4 and FeCI3 solutions. Small Cu and bronze addition (4%) had a positive effect in H_2SO_4 and FeCl3 solutions. layer produced by PM cladding showed similar anodic polarization behavior to the 316L cladding layer in H_2SO_4 and FeCl_3 solutions.