A new metastable β type titanium alloy called TB-13 with the combination of excellent strength and ductility was developed successfully. In order to develop a
【机 构】
:
State Key Laboratory of Solidification Processing,Beijing Institute of Aeronautical Materials
论文部分内容阅读
A new metastable β type titanium alloy called TB-13 with the combination of excellent strength and ductility was developed successfully. In order to develop a perspective on this new alloy, the influence of several commonly used heat treatments on the microstructure and properties was studied. In solution-treated and quenched samples, a low-temperature aging at 480 ℃ results in the precipitation of finer α phase. The precipitation of coarser α phase plate at higher aging temperature (560 ℃) leads to the increase of tensile ductility but reduction of strength. During low-temperature aging at 300 ℃, quite homogeneous distribution of fine isothermal ω phase particles was found. The isothermal ω phase provides nucleation sites for α phase during two-step aging process and makes α phase extremely fine and disperse uniformly in β matrix. Thus, TB-13 alloy is strengthened and its mechanical properties are improved.
其他文献
Mg粉在800℃氨气流中氨化60 min,可得到高质量的Mg3N2粉末.XRD分析表明,Mg3N2粉末是体心立方结构,晶格常数a=0.996 57 nm.SEM分析表明,Mg3N2粉末有多种形貌.PL测试表明,在激
采用"阶梯"铸件,设计了压铸过程模具温度测量的实验方案并进行了压铸实验.以实验中测得的铸型内部不同位置的温度为基础,采用热传导反算法求解了压铸过程中铸件/铸型界面热流
The feasibility of reducing Cr(VI) from the aqueous solution by sulfuric acid-modified titanium-bearing blast furnace slag (SATBBFS) as a photocatalyst was inve
N-doped ZnO films were radio frequency (RF) sputtered on glass substrates and studied as a function of oxygen partial pressure (OPP) ranging from 3.0-10-4 to 9.
The thermal debinding behavior of stainless steel foam precursor in vacuum was studied and compared with that in hydrogen. The formation cause of pore channel w
The rare earth ternary complex of Eu3+ with thenoyltrifluoroacetone, and 4, 7-2NH2 phenanthroline was synthesized and well characterized by UV, fluorescent, IR
An aluminium alloy and its composite with dispersed SiC particles made by liquid metallurgy route were extruded under optimized conditions.The properties were c
The grain growth morphology, kinetics and texture change after uniaxial compression at 430 ℃ of an extruded AZ31 alloy were studied. The samples were loaded fo
Nanostructured zirconia top coat was deposited by air plasma spray and NiCoCrAlTaY bond coat was deposited on Ni substrate by low pressure plasma spray. Nanostr
The initiation sites and influencing factors of cavity nucleation were investigated for a Ti-6Al-2Zr-1Mo-1V alloy with lamellar starting structure, using the is