SiCp/2024 aluminum alloy matrix composite was prepared by powder metallurgy method. Effects of heat treatment on the microstructure and mechanical properties of composite were investigated by SEM, EDS, XRD, HREM, tensile and hardness tests. The experimental results showed that SiC particles distributed uniformly in the matrix and were in good combination with matrix. The tensile strength and hardness were improved significantly after heat treatment. With the increase of solid solution temperature, the alloy phases dissolved in the matrix gradually. When the solid solution temperature arrived at 505 ℃, the alloy phases dissolved thoroughly, and the composite exhibited the highest tensile strength and hardness(σb=360 MPa, HBS=104). The main strengthening phase was Al_2Cu, which was granular and distributed dispersively in the matrix. Effect of T6 was better than that of T4 at the same solid solution temperature.
Effects of heat treatment on the microstructure and mechanical properties of composite were investigated by SEM, EDS, XRD, HREM, tensile and hardness tests. The experimental results showed that SiC particles distributed uniformly in the matrix and were in good combination with matrix. The tensile strength and hardness were improved significantly after heat treatment. With the increase of solid solution temperature, the alloy phase dissolved in the matrix gradually. , the alloy phases dissolved thoroughly, and the composite exhibits the highest tensile strength and hardness (σb = 360 MPa, HBS = 104). The main strengthening phase was Al 2 Cu, which was granular and distributed dispersively in the matrix. Effect of T6 was better than that of T4 at the same solid solution temperature.