This paper reports that Al1 xInxN epilayers were grown on GaN template by metalorganic chemical vapor de-position with an In content of 7%-20%. X-ray diffraction results indicate that all these Al1 xInxN epilayers have a relatively low density of threading dislocations. Rutherford backscattering/channeling measurements provide the exact compositional information and show that a gradual variation in composition of the Al1 xInxN epilayer happens along the growth direction. The experimental results of optical reflection clearly show the bandgap energies of Al1 xInxN epilayers. A bowing parameter of 6.5 eV is obtained from the compositional dependence of the energy gap. The cathodoluminescence peak energy of the Al1 xInxN epilayer is much lower than its bandgap, indicating a relatively large Stokes shift in the Al1 xInxN sample.
This paper reports that Al1 xInxN epilayers were grown on GaN template by metalorganic chemical vapor de-position with an In content of 7% -20%. X-ray diffraction results indicate that all these Al1 xInxN epilayers have a relatively low density of threading dislocations . Rutherford backscattering / channeling measurements provide the exact compositional information and show that a gradual variation in composition of the Al1 xInxN epilayer happens along the growth direction. The experimental results of optical reflection clearly show the bandgap energies of Al1 x InxN epilayers. A bowing parameter of 6.5 eV is obtained from the compositional dependence of the energy gap. The cathodoluminescence peak energy of the Al1 xInxN epilayer is much less than its bandgap, indicating a relatively large Stokes shift in the Al1 xInxN sample.