【摘 要】
：
Phosphors with ( Ce0. 67 -xGdxTb0. 33 ) MgAl11 O19 (0 ≤ x ≤0.37 ) composition were prepared by sol-gel processing. The preparation process, crystal structure
【机 构】
：
School of Sciences,State Key Laboratory of New Ceramics and Fine Processing
论文部分内容阅读
Phosphors with ( Ce0. 67 -xGdxTb0. 33 ) MgAl11 O19 (0 ≤ x ≤0.37 ) composition were prepared by sol-gel processing. The preparation process, crystal structure and luminescent properties of the phosphor powders were investigated.The excitation spectrum is characteristic of Ce3+ ion, while the emission spectrum is composed of lines from Tb3+ ion with main emission peaks at around 542 nm and 487 nm. As the Gd3 + concentration increases, the luminescent intensity at about 542 nm increases to a maximum when x is about 0.12 and then decreases again at higher concentration of Gd3 +ion, whereas, the luminescence at about 487 nm follows the contrary rule.
其他文献
Pure and rare earth doped gadolinium oxide (Gd2O3) waveguide films were prepared by a simple sol-gel process and dip-coating method. Structure of Gd2O3 films an
The Y2O3: Yb3+ , Er3 + microstructures were fabricated by a hydrothermal method without surfactants.The microstructures structure was characterized by X-ray dif
Co-substituted Ni-Zn ferrite was prepared by a chemical codeposition. The electromagnetic properties, zero reflection conditions and simulated reflection losses
. PZT piezoelectric ceramic with La2O3, SrCO3, BaO and Sb2O5 was prepared. It has high value of the piezoelectric strain constant d33 ( -681 PC/N) and high valu
Ceria- and alumina-pillared interlayered clays were synthesized in the presence of PEO surfactant by using laponite clay as raw material.And the synthesized pil
A series of lanthanum containing Ni-base catalysts were prepared by citric acid complex method.Carbon nanotubes (CNT) were synthesized bY catalytic decomposing
Effects of processing technology on the properties such as relative density, flexural strength, fracture toughness, hardness, etc. and the microstructure of rar
The study of recent years found that big bulk amorphous alloys were formed for some multi-element compositions at rapid cooling speed such as Zr-, La-, Fe-, Mg-
The forming-regions and properties were studied on phosphate system glasses Sm2O3 doped by two step melting method. It shows that with the increasing of rare ea