LiAlH4 doped with Ni and Ce(SO4)2 additives and the effect of doping on temperature and hydrogen release were studied by pressure-content-temperature (PCT) experiment and X-ray diffraction (XRD) analysis. It is indicated that doping with Ni induces a significant decrease in temperature in the first step and LiAlH4 doped with 1mol% Ni presents the most absorption of hydrogen. Doping with Ce(SO4)2 also causes a marked decrease, while the amount of hydrogen release changes only slightly. The results from X-ray diffraction analysis show that doping does not cause any structural change; Ni and Ce-containing phases are not observed at room temperature or even at 250°C.
LiAlH4 doped with Ni and Ce (SO4) 2 additives and the effect of doping on temperature and hydrogen release were studied by pressure-content-temperature (PCT) experiment and X-ray diffraction (XRD) analysis. It is indicated that doping with Ni induces a significant decrease in temperature in the first step and LiAlH4 doped with 1 mol% Ni presents the most absorption of hydrogen. Doping with Ce (SO4) 2 also causes a marked decrease, while the amount of hydrogen release changes only slightly. X-ray diffraction analysis show that doping does not cause any structural change; Ni and Ce-containing phases are not observed at room temperature or even at 250 ° C.