The magnetic properties of Fe3(1-x)Cr3xC alloys with x=0.05, 0.1, 0.15, and 0.2, which crystallize in the cementite Fe3C-type structure with space group Pnma, were investigated by means of magnetization measurements. These alloys show temperature-induced second-order magnetic phase transitions. The Curie temperature (Tc) of these alloys decreases with increasing x. The isothermal magnetic-entropy changes of these alloys were derived from the magnetic isotherms measured with increasing tem-perature and increasing field. The maximum values of the magnetic-entropy change are about 0.9 and 3.6 J·kg-1·K-1 at Tc =360 K for x = 0.05 in a magnetic field change from 0 to 1 T and 0 to 5 T, respectively.
The magnetic properties of Fe3 (1-x) Cr3xC alloys with x = 0.05, 0.1, 0.15, and 0.2, which crystallize in the cementite Fe3C-type structure with space group Pnma, were investigated by means of magnetization measurements. These alloys show temperature The isothermal magnetic-entropy changes of these alloys were derived from the magnetic isotherms measured with increasing tem-perature and increasing field. The maximum values of the magnetic-entropy change are about 0.9 and 3.6 J · kg-1 · K-1 at Tc = 360 K for x = 0.05 in a magnetic field change from 0 to 1 T and 0 to 5 T, respectively.