研究了挂浆法制备泡沫镍的浆料配置工艺,通过粘度测定和浆料沉降实验评价了粘结剂和分散剂含量以及固含量对浆料流变行为和稳定性的影响。结果表明,当浆料中的粘结剂与分散剂含量分别控制在3%~4%与0.2%~0.4%时,固含量达到30%~40%;采用挂浆法浸渍泡沫所得泡沫镍前驱体的孔筋粗细均匀,且其三维通孔性良好。 The slurry configuration technology for the production of nickel foam was studied. The influence of the content of binder and dispersant and the solid content on the rheological behavior and stability of the slurry were evaluated by viscosity measurement and slurry sedimentation experiments. The results show that when the content of binder and dispersant in slurry is controlled at 3% ~ 4% and 0.2% ~ 0.4% respectively, the solid content reaches 30% ~ 40% The body of the tendons uniform thickness, and good three-dimensional through-hole.