The microstructure and elevated-temperature mechanical properties of dispersoid-strengthened Al-Mg-Si-Mn al-loys produced by twin roll casting (TRC) and conventional mold casting (MC) were studied.A specific heat treatment at 430 ℃ for 6 h was applied,fol
【机 构】
：
State Key Laboratory of Rolling and Automation,Northeastern University,Shenyang,110819,China;Guangxi
论文部分内容阅读
The microstructure and elevated-temperature mechanical properties of dispersoid-strengthened Al-Mg-Si-Mn al-loys produced by twin roll casting (TRC) and conventional mold casting (MC) were studied.A specific heat treatment at 430 ℃ for 6 h was applied,followed by rolling.Tensile tests were carried out at 300 ℃.The results show that in the as-cast microstructures,equiaxed grains formed in the MC sample while elongated grains with substructures formed in the TRC sample.The eutectics in the TRC sample were much finer than those in the MC sample.Upon heat treatment,large numbers of α-Al(Fe,Mn)Si dispersoids precipitated,and the TRC sample had a greater number density of dispersoids than those in the MC sample.During the tensile test after rolling,the TRC samples exhibited higher strength than the MC samples,which resulted from the combination of the strength-ening effect of the stronger dispersoids and the greater substructure hardening effect in the TRC sample;the TRC sample exhibited better ductility due to its finer initial eutectic than that in the MC sample,which depressed the stress concentration and delayed the occurrence of microcracks and fracture in the TRC sample.
其他文献
Combination of hot isostatic pressing (HIP) and rejuvenation heat treatment (RHT) technology was used to restore creep-damaged DZ125 directional solidified superalloy,and the influence of microstructure restoration on high temperature fatigue behavior of
CeO2-ZrO2 mixed oxides with controlled morphologies (i.e.,nanorod,nano-polyhedral and disordered shape)were synthesized through either hydrothermal or coprecipitation method,and the corresponding supported Pd/CeO2 ZrO2 catalysts were also prepared by conv
As a candidate material for hydrogen separation,Yb-doped SrCeO3 has attracted increasing attention in recent decades.In the present study,Yb-doped SrCe0.9Yb0.1O3-α ceramics were prepared by the dry pressing and sintering approach,with the microstructure e
The crosslinked gelatin/chitosan/poly(vinyl alcohol)/hydroxyapatite (GEL/CTS/PVA/HAp,GCPH) sponges were fabricated by a freeze-drying method to yield the reinforced composite sponges with proper features.The porosity value and pore size of the crosslinked
The influence of heat treatments on the microstructures and mechanical properties of the selective laser melting manufactured AlSi10Mg alloy modified with Sc was systematically investigated.The results showed that the addition of Sc element introduced pri
Effects of Al addition to a Mg-Sn-Ca ternary alloy on its microstructure and tensile properties after extrusion were studied via extrusion of Mg-1.0Sn-0.5Ca-xAl (x =0,0.8,2.4 wt％) sheets and analysis of the extruded materials.The results showed that Al ad
In this work,Cu/Al8011/Al1060 trilayered composite with an ultrathin copper layer was fabricated successfully by the hybrid process of cast-rolling and hot-roll-bonding.The effects of heat treatment were investigated on the microstructure and mechanical b
为了提高高三复习课的实效性,回归课本是高三复习的正道,问题引领复习探究的方向,变式教学是复习教学的有效策略.文章通过“问题引领回归课本”和“自然变式微型探究”引导学生积极参与,深度思考,提升了学生发现问题、提出问题、分析问题和解决问题的能力.