A new technology, the two-step transient liquid phase diffusion bonding (TLP-DB) technology for cobalt-based K640 superalloy, was investigated. The method consists of a short-time high temperature heating to melt interlayer followed by isothermal solidification of liquid phase at a lower temperature than that of the conventional TLP-DB. The result indicates that the two-step TLP-DB can reliably produce an ideal joint with uniform chemical composition, which is superior to the joint welded by conventional TLP-DB in microstructure and mechanical properties. Bonding parameters of new process are 1 250 ℃ for 0.5 h and 1 180 ℃ for 3 h. The high-temperature tensile strength of the joint by two-step TLP-DB reaches 74% of that of the base material on an equal basis, but the high-temperature tensile strength of the joint by conventional TLP-DB is only 58% of that of the base material.