研究Ni-Mo-Fe型铸造镍基合金的组织及其耐蚀性能。针对30—36%HCl,50℃苛刻介质,与其性能优良的HastelloyB—2做了对比试验。着重研究了W对该合金组织与耐蚀性能的影响。
The microstructure and corrosion resistance of Ni-Mo-Fe cast Ni-base alloy were studied. For 30-36% HCl, 50 ℃ harsh media, and its performance HastelloyB-2 made a comparative test. The effect of W on the microstructure and corrosion resistance of the alloy was studied emphatically.