CeO2-TiO2 films and CeO2-TiO2/SnO2:Sb(6 mol%)double films were deposited on glass substrates by radio-frequency magnetron sputtering(R.F.Sputtering),using SnO2:
【机 构】
：
Key Laboratory of Silicate Materials Science and EngineeringWuhan University of Technology
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
CeO2-TiO2 films and CeO2-TiO2/SnO2:Sb(6 mol%)double films were deposited on glass substrates by radio-frequency magnetron sputtering(R.F.Sputtering),using SnO2:Sb(6 mol%)target,and CeO2-TiO2 targets with different molar ratio of CeO2 to TiO2 (CeO2:TiO2=0:1.0;0.1:0.9;0.2:0.8;0.3:0.7;0.4:0.6;0.5:0.5;0.6:0.4; 0.7:0.3; 0.8:0.2;0.9:0.1;1.0:0).The films are characterized by UV-visible transmission and infrared reflection spectra,scanning electron microscopy(SEM),Raman spectroscopy,X-ray photoelectron spectroscopy(XPS)and X-ray diffraction(XRD),respectively.The obtained results show that the amorphous phases composed of CeO2-TiO2 play an important role in absorbing UV, there are Ce3+,Ce4+ and Ti4+ on the surface of the films;the glass substrates coated with CeO2-TiO2(Ce/Ti=0.5:0.5;0.6:0.4)/SnO2:Sb(6 mol%) double films show high absorbing UV(>99),high visible light transmission(75%)and good infrared reflection films can be used as window glass of buildings,automobile and so on.
其他文献
To provide theoretical basis and practical guidance for preparing composite rods of external diameter no larger than 12 mm by directly continuous casting,low me
Rare earth element (REE) concentrations were measured by ICP-MS for groundwater collected from deep seated Taiyuan Fm limestone aquifer (from -400 to -530 m) in
Vertically aligned ZnO nanorods were synthesized on a-plane sapphire via a metal catalyzed vapor phase transport and condensation process in a two-zone vacuum f
为确保辐射测量精度，需要对红外辐射测量系统进行标定。在分析红外辐射测量系统工作原理的基础上，提出了内、外标定相结合的标定方法，区别于传统的标定方法，不再把测量系统当作“
The value of spin-orbit splitting Δ0 of gallium phosphide (GaP) nanoparticles was determined.The information concerning the spin-orbit splitting of the valence
The antiwear and friction-reducing performances of sodium borate, potassium borate and lanthanum chloride in water were evaluated on a four-ball friction tester
刘金广，1958年出生，本科学历，1980年参加工作，先后在顺义区木林中心小学、木林中小、顺义区石园小学任教导主任、副校长、校长，2008年6月调任顺义东风小学任校长至今。
This paper discusses some previous, and presents some new experimental results on wave transmission over submerged breakwaters. The objective of this study is t
Calcium sulphoaluminate was prepared with chemical reagents in this paper.The formation mechanism of calcium sulphoaluminate and effect of CuO on the formation
Free spanning pipelines are suspended between two points on an uneven seafloor. The variations of structural conditions, such as the changes in soil property, f