论文部分内容阅读
用模具挤出的方法制备了蜂窝式0.98%V_2O_5-9 65%WO_3/TiO_2的SCR脱硝催化剂,采用BET、XRD、SEM、XRF等方法对微观结构进行考察.在SCR脱硝试验装置上测试各种条件下催化剂的性能,并与结构类似的商业催化剂进行对比.通过试验发现,在空速比(SV)为4 000 h~(-1)、NH_3/NO=0.9～1.0、300～400 ℃范围内,自制催化剂的NO脱除率、SO_2氧化率、N_2O生成率和氨逃逸量,与商业催化剂相比性能接近,基本达到商业应用的要求.在水蒸气含量超过5%时对NO脱除率影响不大,因此催化剂适用于实际烟气.试验中未观察到SO_2对NO脱除的促进作用.自制催化剂结构强度低于商业催化剂,有待进一步改进.“,”By employing a die set extrusion method,prepared was a honeycomb type 0.98%V_2O_5-9.65%WO_3/TiO_2-contained SCR(selective catalytic reduction) catalyst.By using BET(brunauer-emmett-teller),XRD(X-ray diffractometer),SEM(scanning electron microscope) and XRF(X-ray fluorescence) method etc.,inspected and explored was the microstructure.On a SCR denitration test rig,tested was the performance of the catalyst under various conditions and conducted was a comparison with commercial catalysts having a similar structure.Through tests,it has been found that when the space velocity(SV) equals to 4 000 h~(-1) and NH_3/NO ratio is 0.9 to 1.0 at a temperature within a range from 300 to 400 ℃,under such circumstances,NO removal rate,SO_2 oxidation rate,N_2O formation rate and ammonia escape quantity of the self-prepared catalyst are comparatively close in performance to those of commercial catalysts,basically meeting the requirements for commercial applications.When the steam content is in excess of 5%,it has little influence on the NO removal rate,thus applicable for practical flue gases.During the tests,it has not been observed that SO_2 played a role of promoting the elimination of NO.The structural strength of the self-prepared catalyst is lower than that of the commercial catalysts,necessitating further improvement.