The pressing bonding of steel plate with QTi3.5-3.5graphite slurry was studied. The relationship among preheating temperature of steel plate, preheating temperature of dies, solid fraction of QTi3.5-3.5graphite slurry, and interfacial shear strength of bonding plate could be established with artificial neural networks perfectly. This model could be optimized with a genetic algorithm. The results show that the optimum bonding parameters are: 618℃ for preheating temperature of steel plate, 526℃ for preheating temperature of dies and 46.2% for solid fraction of QTi3.5-3.5graphite slurry, and the largest interfacial shear strength of bonding plate is 128.3 MPa.
The relationship among preheating temperature of steel plate, preheating temperature of dies, solid fraction of QTi3.5-3.5graphite slurry, and interfacial shear strength of bonding plate could be established with artificial neural networks perfectly. This results could be optimized with a genetic algorithm. The results show that the optimum bonding parameters are: 618 ° C for preheating temperature of steel plate, 526 ° C for preheating temperature of dies and 46.2% for solid fraction of QTi3.5-3.5graphite slurry, and the largest interfacial shear strength of bonding plate is 128.3 MPa.