A Raman study was carried out for LiMn 2O 4, which was synthesized via the mixture of Mn 3O 4 and LiNO 3 sintered at different temperatures. It is shown that there are two kinds of Raman spectra for LiMn 2O 4 at different sintering temperatures, while the X-ray diffraction patterns of LiMn 2O 4 sintered at different temperatures are the same. Five Raman bands observed for the materials sintered below 500 ℃ are consistent with the theoretical prediction for spinel structure based on the group theory. Only two Raman bands were observed for the materials sintered at temperatures higher than 500 ℃. The best preparation condition for obtaining a good spinel LiMn 2O 4 is suggested based on the Raman study. A Raman study was carried out for LiMn 2O 4, which was synthesized via the mixture of Mn 3O 4 and LiNO 3 sintered at different temperatures. It is shown that there are two kinds of Raman spectra for LiMn 2O 4 at different sintering temperatures, while the X-ray diffraction patterns of LiMn 2O 4 sintered at different temperatures are the same. Five Raman bands observed for the material sintered below 500 ° C. are consistent with the theoretical prediction for spinel structure based on the group theory. Only two Raman bands were observed for the materials sintered at temperatures higher than 500 ° C. The best preparation condition for obtaining a good spinel LiMn 2O 4 is suggested based on the Raman study.