【摘 要】
:
Ce0.6Zr0.4O2 solid solution was prepared by co-precipitation technique using hydrazine hydrate as precipitator.Various physico-chemical techniques such as XRD,
【机 构】
:
School of Chemistry and Material Sciences
论文部分内容阅读
Ce0.6Zr0.4O2 solid solution was prepared by co-precipitation technique using hydrazine hydrate as precipitator.Various physico-chemical techniques such as XRD, FT-Raman, SEM, TEM, etc.were used to characterize the resultant powder.Meanwhile, its catalytic activity was evaluated in the synthesis of n-butyl acetate by the reaction of acetic acid and n-butyl alcohol.The results show that ceria-zirconia solid solution forms single cubic structure and its particle diameter is less than 100 nm.As a sort of solid acid, it possesses high catalytic activity and can be easily separated from reaction liquid.After it is used for ten times, its activity basically kees unchanging.
其他文献
Dy-Fe alloy replace dysprosium in the NdFeB permanent material can improve the performance and productivity and cut the cost.The electrolyte is a binary system
The synchrotron X-ray double-crystal topography was employed to investigate the structure of Si/SiGe/Si deposited on SIMOX SOI. Rocking curves with three diffra
In liquid-liquid solvent extraction processes, diluents have a strong influence on the extraction mechanism and efficiency. In this study, benzene, cyclohexane,
Magnesium alloys are widely used as shells of 3C (computer, mobile phone and consumer electronics) equipments for its impressive mechanical and physical propert
The special ultrasonic testing system has been developed for thickness measurement of plasma sprayed coatings. The ultrasonic immersion method was used to obtai
Carbon foam-a kind of new engineering material as packing material was adopted in three biofilters with different pore dimensions and adapted autotrophic nitrit
The magneto-caloric effect of Gd5 Si2Ge2 compounds produced by various techniques is investigated in terms of their magnetization behaviors in the magnetic fiel
SiGe-on-Insulator (SGOI) is an ideal substrate material for realizing strained-silicon structures that are very competing and popular in present silicon technol
Eu2Mn2/3Ta4/3O7 specimen was synthesized from Eu2O3, MnO and Ta2O5 in a reducing atmosphere. Structure analysis was carried out by Rietveld method from X-ray di