【摘 要】
：
X80 pipeline steel plates were friction stir welded (FSW) under air,water,liquid CO2 + water,and liquid CO2 cooling conditions,producing defect-free welds.The microstructural evolution and mechanical properties of these FSW joints were studied.Coarse gran
【机 构】
：
State Key Laboratory of Rolling and Automation,Northeastern University, Shenyang 110819, China;Sheny
论文部分内容阅读
X80 pipeline steel plates were friction stir welded (FSW) under air,water,liquid CO2 + water,and liquid CO2 cooling conditions,producing defect-free welds.The microstructural evolution and mechanical properties of these FSW joints were studied.Coarse granular bainite was observed in the nugget zone (NZ) under air cooling,and lath bainite and lath martensite increased significantly as the cooling medium temperature reduced.In particular,under the liquid CO2 cooling condition,a dual phase structure of lath martensite and fine ferrite appeared in the NZ.Compared to the case under air cooling,a strong shear texture was identified in the NZs under other rapid cooling conditions,because the partial deformation at elevated temperature was retained through higher cooling rates.Under liquid CO2 cooling,the highest transverse tensile strength and elongation of the joint reached 92％ and 82％ of those of the basal metal (BM),respectively,due to the weak tempering softening.A maximum impact energy of up to 93％ of that of the BM was obtained in the NZ under liquid CO2 cooling,which was attributed to the operation of the dual phase of lath martensite and fine ferrite.
其他文献
The microsegregation behavior of the Al-4.5 wt％Cu alloy solidified at different cooling rates under the alternating magnetic field (AMF) was investigated.The experimental results showed that the amount of non-equilibrium eutectics in the interdendritic re
The effect of a pulsed electric current on the residual stress evolution of metal materials has been investigated.It was found that the surface and internal residual stresses in the as-quenched samples were reduced dramatically by electropulsing.A large n
A 2.5-mm Fe72.5B15.6Si7.8Nb1.7Zr1.7Cu0.7 glassy rod was successfully fabricated using copper mold casting.The introduction of Cu resulted in the formation of large quantities of α-Fe nanoparticles embedded in the glassy matrix after isothermal annealing.T
A systematic study of nitric acid passivation was investigated to enhance the general corrosion resistance of biomedical high-nitrogen nickel-free stainless steels (HNSs).After passivation,the corrosion rate of HNS could dramatically reduce to 1/20 of the
The void formation and plastic deformation micromechanisms of a cold-rolled DP600 steel during tensile loading were studied by scanning electron microscopy (SEM) and electron backscatter diffraction (EBSD).The SEM observations revealed that the main void
Mg alloys,as a new generation of biodegradable bone implant materials,are facing two tremendous challenges of enhancing strength and reducing degradation rate in physiological environment to meet clinical needs.In this study,tricalcium phosphate (β-TCP) p
Friction stir additive manufacturing is a newly developed solid-state additive manufacturing technology.The material in the stirring zone can be re-stirred and reheated,and mechanical properties can be changed along the building direction.An integrated mo
T6-treated 20 wt％ B4Cp/6061Al sheets were joined under welding speeds of 400-1200 mm/min by friction stir welding (FSW) with a threaded cermet pin.The macro-defect-free FSW joints could be achieved at high welding speeds up to 1200 mm/min,but larger plung
W-Y2O3 composite nanopowders prepared via wet chemical method exhibit unique morphologies and microstructures.The yttrium addition during chemical reaction process affects not only the composition of tungsten acid hydrate precursors,but also the reduction
In this work,the influence of the Zener-Hollomon (Z) parameter on the microstructure and mechanical properties of copper subjected to friction stir welding (FSW) was investigated.Liquid N2 cooling was conducted to control the cooling rate after the FSW.Th