【摘 要】
：
Asphaltene-ceramic composite membranes were fabricated from ceramic supports and an asphaltene component,which was obtained from the separation of coal to give
【机 构】
：
School of Chemical Engineering and Technology
论文部分内容阅读
Asphaltene-ceramic composite membranes were fabricated from ceramic supports and an asphaltene component,which was obtained from the separation of coal to give a kind of new carbonaceous precursor material.Using SEM and thermogravimetric analysis to measure the microstructure and properties of the asphaltene component allowed the porosity,permeability,and retention ratios to be determined.The results show that the asphaltene component can be regarded as a good carbon membrane precursor material because of its high carbon content and strong bonding capacity.When ceramic supports are impregnated with asphaltene colloid the asphaltene easily combines with the support surface and forms a good carbonaceous film after carbonization.Little of the asphaltene component permeates into the internal pores of the ceramic support.Although the number of coats applied to the substrate had little affect on the porosity of the asphaltene-ceramic composite membranes the permeability varied depending upon the number of times the substrate was treated.The way bubbles escape from the film.and the phenomenon of coalescence,as affected by different film thicknesses also seem closely related to the number of coats.A composite membrane carbonized at a final temperature of 600 ℃ is relatively dense and the permeability of Fe(OH)3 colloid through it is very low.A membrane fired at 800 ℃ is porous and its permeability and retention of Fe(OH)3 colloid are 88 L/(m2 h MPa) and 85.3％,respectively when the trans-membrane pressure is 0.22 MPa.
其他文献
Solid-liquid equilibrium of quaternary system Cd, SO-HO at 298 K was studied by means of an isothermal solution saturation method. Experimental results indicate
A novel type of crosslinkable poly(aryl ether sulfone)(PAES) bearing an allyl pendant(PES-OAllyl) was synthesized by a grafting reaction of hydrophenyl-containi
CeVO4, CeMo0.01 V0.99O4 and CeMo0.03V0.97O4 were prepared by co-precipitation method. The addition of molybdenum as promoter shows a positive effect on the cata
In this work, we propose a new spin-coating method coupling with high thermal decomposition, to prepare the tin-antimony (Sn-Sb) oxide electrode. The character
A series of novel neonicotinoids derivatives 4a-4p was designed and synthesized by introducing the ethylbenzene group into the thiazole ring, their structures w
Let Mn be an n-dimensional complete connected and oriented hypersurface in a hyperbolic space Hn+1(c) with non-zero constant mean curvature H and two distinct p
The novel nickel-based catalysts with a nickel content of 12 wt% were prepared with the zirconia-alumina composite as the supports. The new carriers, ZrO2 impro
A facile approach for the synthesis of gold nanoparticle-loaded carbon nanofiber(Au/CNF) composites was developed. When applied to electrochemistry, these compo
The authors consider the homogenization of a class of nonlinear variational inequalities, which include rapid oscillations with respect to a parameter. The homo
Let N be a sufficiently large even integer. Let p denote a prime and P2 denote an almost prime with at most two prime factors. In this paper, it is proved that