契诺波维斯基冶金厂掌握了在双床平炉强制吹氧冶炼无时效钢08铝的工艺。基本工艺参数如下:铁水消耗大约62％,熔池兑铁水后吹氧(20—30米~3/小时·吨),氧枪保持在铁水—渣界面处,在钢水中碳含量达～0.1％时停止吹氧。钢水在炉内和盛钢桶内用锰铁脱氧并用外口孔径为80毫米的浇注水口在上小下大扁钢锭桶内浇注成重14—16吨的扁锭。用一次
Cincinnati Pivovsky Metallurgical Plant mastered the technology of ORE 08 08 aluminum without forced aging in a double hearth furnace. The basic process parameters are as follows: the molten iron consumption is about 62%, the molten steel blows oxygen (20-30 m 3 / h · t) after the molten iron, the oxygen gun remains at the molten iron-slag interface, and the carbon content reaches ~ 0.1% Stop blowing oxygen. Molten steel in the furnace and the ladle with ferromanganese deoxidation and the outer port with a hole diameter of 80 mm in the upper and lower large flat steel ingot barrel poured into heavy 14-16 tons of ingot. Use once