Tungsten inert gas(TIG) arc-assisted laser welding–brazing was used for the butt joining of 5A06 aluminum alloy to the galvanized steel by preset filler powder without groove. The spreading behavior of liquid metal on the back of the galvanized steel at different assisted welding currents was also investigated. The results show that the assisted TIG arc optimizes the interface reaction temperature, enhances the wettability of liquid metal on the steel side, and forms a sound butt joint at an appropriate welding current. A non-uniform intermetallic compound is formed at the interfacial layer, which is composed of Fe2Al5 close to the steel substrate and Fe4Al13 close to the solidified aluminum. The superior tensile strength of joint is indicated when the welding current ranges from 13 to 16 A. The average tensile strength can reach 151 MPa at the welding current of 16 A, and the corresponding fracture belongs to the ductile and brittle hybrid mode. Tungsten inert gas (TIG) arc-assisted laser welding-brazing was used for the butt joining of 5A06 aluminum alloy to the galvanized steel by preset filler powder without groove. The spreading behavior of liquid metal on the back of the galvanized steel at different assistance welding results was also investigated. The results show that the assisted TIG arc optimizes the interface reaction temperature, enhances the wettability of liquid metal on the steel side, and forms a sound butt joint at an appropriate welding current. A non-uniform intermetallic compound is formed at the interfacial layer, which is composed of Fe2Al5 close to the steel substrate and Fe4Al13 close to the solidified aluminum. The superior tensile strength of joint is indicated when the welding current ranges from 13 to 16 A. The average tensile strength can reach 151 MPa at the welding current of 16 A, and the corresponding fracture belongs to the ductile and brittle hybrid mode.