【摘 要】
：
分别由两种不同种类的胶粘剂制取复合胶粘剂,并由该复合胶粘剂制取型焦,根据型焦的各项性能优选复合胶粘剂。实验结果表明,优选的复合胶粘剂是由无机水玻璃和有机聚乙烯醇(PV
【机 构】
：
西安建筑科技大学贵金属工程研究所,陕西省冶金工程技术研究中心,
论文部分内容阅读
分别由两种不同种类的胶粘剂制取复合胶粘剂,并由该复合胶粘剂制取型焦,根据型焦的各项性能优选复合胶粘剂。实验结果表明,优选的复合胶粘剂是由无机水玻璃和有机聚乙烯醇(PVA)混合而成;当W(复合胶粘剂)=13%时,型焦的各项性能达到最佳值,其冷热强度分别为4.98 MPa和2.55 MPa,固定碳含量为76.42%。
The composite adhesive is prepared from two different types of adhesives respectively, and the type of coke is prepared from the composite adhesive. The composite adhesive is preferably selected according to the properties of the type coke. The experimental results show that the preferred composite adhesive is a mixture of inorganic water glass and organic polyvinyl alcohol (PVA); when W (composite adhesive) = 13%, the performance of the coke to achieve the best value, the hot and cold The intensities were 4.98 MPa and 2.55 MPa respectively, and the fixed carbon content was 76.42%.
其他文献
本文研究具有Bernoulli反馈和负顾客到达的多重休假M/G/1排队系统,负顾客抵消队首的正顾客,完成服务的正顾客以概率θ(0
目的 通过荧光偏振免疫测定(fluorescence polarization immunoassay,FPIA)和酶放大免疫测定技术(enzyme-multiplied immunoassay technique,EMIT)测定环孢素A(cyciosporine,
Al/Ti反应多层膜中反应区的传播速度是表征其特性的特征参数之一.通过定义初始单层厚度比为δ:(2b-1)δ,将Mann模型扩展为可计算任意厚度比的多层膜中反应区的传播速度.采用
合成了含NOS配位原子的三齿西夫碱的镍配合物,并用红外,核磁,元素分析和晶体衍射进行了表征.发现此类配合物在相转移试剂存在下以次氯酸钠为氧源对烯烃的氧化具有较好的催化
目的 探讨caspase 12在强噪声诱导的豚鼠耳蜗细胞凋亡中的作用.方法 选用健康雄性白色豚鼠32只,随机数字表法分为4组,将实验组动物暴露于声压级120 dB、4 kHz窄带噪声环境4 h
制备色谱通过放大可以直接作为工业规模的分离工具。因此,制备色谱分离参数的优化具有重要意义。在实用中最关键的操作参数是进样浓度、进样体积与流动相流率,尤其是前两者直
研究了Sr对Mg-5Al-0.8Ca-0.2La镁合金显微组织与室温和高温力学性能的影响.实验结果表明,Sr的加入显著细化了基体合金的显微组织,抑制了β-Mg17Al12相的析出;并且在晶界上析
在Moor-Shannon网络模型中,k限制边连通度较大的网络一般有较好的可靠性和容错性.本文在无向Kautz图UK(2,n)中研究k限制边连通度的上界ξk,证明了ξ5(UK(2,3))=6,ξ5(UK(2,n)
本文证明了一类含权Rellich不等式,其中的常数是最佳的.
采用密度泛函理论(DFT)中B3LYP方法,在Lanl2dz水平下对PtnNim(n+m≤5,n,m≠0)团簇进行了结构优化,预测它们的基态几何结构,并对基态结构的平均结合能、磁性以及五个原子团簇