不锈钢钢板在热轧工序易因轧辊与钢板粘结而产生表面损伤 ,对此以往采用加轧制油、改变轧辊材质或调整轧制温度等对策。但是 ,耐高温氧化性优良的不锈钢 ,热轧时生成的氧化铁皮极少 ,易出现表面损伤。为解决上述问题 ,日本川崎钢铁公司提出在板坯上涂敷氧化促进剂 ,增加轧制氧 Stainless steel plate in the hot-rolled process easy to roll and plate adhesion to the surface damage, which used to add rolling oil, change the roll material or adjust the rolling temperature and other measures. However, stainless steel excellent in high-temperature oxidation resistance generates very few scale pieces during hot rolling and easily causes surface damage. In order to solve the above problems, Japan Kawasaki Steel proposed the application of oxidation promoter on the slab to increase rolling oxygen