采用高功率CO2激光对新型稀土镁合金NZ30K进行焊接,对3种不同厚度试板在合适的焊接参数下得到的焊接接头微观组织和力学性能进行了分析和测试。结果表明,在合适的激光焊接工
论文部分内容阅读
采用高功率CO2激光对新型稀土镁合金NZ30K进行焊接,对3种不同厚度试板在合适的焊接参数下得到的焊接接头微观组织和力学性能进行了分析和测试。结果表明,在合适的激光焊接工艺参数下,不同厚度的试板都可以得到成形良好的焊缝;不同厚度的试板得到的焊缝组织不同,从而使其焊接接头的拉伸性能产生差异。
The new rare earth magnesium alloy NZ30K was welded by high-power CO2 laser. The microstructure and mechanical properties of the welded joints obtained under suitable welding parameters were analyzed and tested for three kinds of test plates of different thicknesses. The results show that under the appropriate laser welding process parameters, the test specimens with different thicknesses can get the well-formed welds. The weld joints with different thicknesses are different, which leads to the difference in the tensile properties of the welded joints.
其他文献
采用共价键合方法，制备了支化聚乙烯亚胺修饰的新型毛细管开管柱，并对其电色谱性能进行了详细研究。结果表明：所制备的修饰固定相，兼具接枝聚合立体构型和丰富的支化高聚物位点，柱
根据冷镦钢ML40Cr的特点,在某公司进行了加热温度、加热时间、轧制过程温度和轧件冷却速度控制等试验研究.结果表明,在加热温度1040℃±25℃、开轧温度980℃±20℃、进精轧机
采用Gleeble-1500热模拟试验机在不同的峰值温度条件下对2.25Cr1Mo0.25V钢焊接热影响区组织与性能进行模拟研究。通过金相及断口分析,研究与讨论了热循环峰值温度对2.25Cr1Mo
生物止血剂样品经过沉淀蛋白、浓缩、提取处理后，用分光光度法测定其中聚山梨酯80的残留量。聚山梨酯80的质量浓度在170 mg·L-1以内与其吸光度呈线性关系，方法具有良好的特异
提出了采用开管毛细管电色谱-电致化学发光联用法测定丙嗪盐酸、盐酸氯丙嗪和盐酸二氧丙嗪的含量。在最优分离条件下，丙嗪、氯丙嗪和二氧丙嗪得到良好的分离，其线性范围均为8．0
基于2-甲基-3-丁烯腈键合开管柱，提出了采用毛细管电色谱法测定中草药中盐酸小檗碱、原阿片碱和延胡索乙素含量的方法。选择分离电压为16 kV，以pH 4．5的30 mmol·L-1磷酸盐缓冲
针对航空轮的结构特征,设计了等温成形工艺方案。采用7A04铝合金进行了试验,并对锻出的航空轮进行了力学性能检测。结果表明,其抗拉强度最高为585MPa,最低为517MPa,屈服强度
应用疏水聚(OMA-co-EDMA-co-SPMA)毛细管整体柱，提出了快速分离头孢菌素类抗生素(头孢哌酮、头孢呋辛、头孢噻吩和头孢克肟)的加压毛细管电色谱分析方法。在优化的色谱条件下，
基于苯丙氨基键合开管柱，提出了开管毛细管电色谱-紫外检测联用法快速测定牛胸腺 DNA总甲基化水平。以pH 2的10 mmol·L-1磷酸盐缓冲溶液与乙腈按体积比45比55混合的 溶液
通过对支架类的零件冲压成型工艺分析,确定了高效率的冲压工艺方案,并完成了该零件的冲压模具设计。重点介绍了在切弧工序模具中磁铁定位和可调换定位板的作用。磁铁定位和可