【摘 要】
：
Thin films of Nd3+/V5+-cosubstituted bismuth titanate,(Bi3.5Nd0.5)( Ti2.96V0.04)O12 (BNTV),were fabricated on the Pt(111)/Ti/SiO2/Si(100) substrates by a chemic
【机 构】
：
Faculty of Materials and Optoelectronic Physics,Key Laboratory of Advanced Materials and Rheological
论文部分内容阅读
Thin films of Nd3+/V5+-cosubstituted bismuth titanate,(Bi3.5Nd0.5)( Ti2.96V0.04)O12 (BNTV),were fabricated on the Pt(111)/Ti/SiO2/Si(100) substrates by a chemical solution deposition technique and annealed at different temperatures of 650,700,750 and 800 ℃. The surface morphology and ferroelectric properties of the samples were studied in detail. The result shows that the film annealed at 800 ℃ indicates excellent ferroelectricity with a remanent polarization of 2Pr=40.9 ìC/cm2,a coercive field (EC) of 114 kV/cm at an applied electrical field of 375 kV/cm. The substitution of Ti-site ion by V5+ ions could improve the upper limit of the optimal annealing temperature by decreasing the space charge density in BNT thin film. Additionally,the mechanism concerning the dependence of ferroelectric properties of BNTV thin films on the annealing temperature was discussed.
其他文献
The main object of the present research is to make a quantitative evaluation on the microstructure of carbon materials in terms of microcrystal. The digitized i
To investigate the treating parameters influence on the surface roughness of the MAO ceramic coating on AZ91D, experiments were implemented in the alkaline elec
Al2O3/TiAl composites were fabricated by PAXD (pressure-assisted exothermic dispersion) method. The effects of Nb2O5 content on the microstructure and mechanica
Through the addition of rare earth oxides into the coating of electrodes, the high temperature oxidation and sulphidation resistance of weld metal were studied.
Effect of cooling rate on both microstructure and room temperature compressive performance of the AZ91 magnesium alloy was investigated. The experimental result
Honeycomb-like superstructures consisting of ZnS nanosheets with uniform thickness of about 20nm and lateral dimension of several micrometers were built up from
For large-sized AISI P20 steel block used as plastic die with a thickness of more than 200 mm, appropriate quenching processes are the key to obtain much thick
Mg65Cu25Gd10 amorphous alloy powders were synthesized by mechanical alloying (MA). The most suitable process is that the milling velocity is 600 r/min and the m
The evolution of configurations of Aln (n=3,4,6,13,19) clusters were investigated using linear synchronous transit (LST) method. The stable structures of Al3,Al
Under electron beam irradiation, the in-situ formation of 2H-SiC dentritic nanocrystals from amorphous silicon carbide at room temperature was observed. The hom