【摘 要】
：
本文采用定量金相方法确定固溶温度、冷却速度与γ′析出相含量及尺寸分布之间的定量关系,为确定热处理工艺提供依据。结果表明,固溶温度升高,γ′析出量增加,并且在1120℃达
论文部分内容阅读
本文采用定量金相方法确定固溶温度、冷却速度与γ′析出相含量及尺寸分布之间的定量关系,为确定热处理工艺提供依据。结果表明,固溶温度升高,γ′析出量增加,并且在1120℃达到峰值;超过此温度则γ′含量降低。300℃盐浴等温较水冷和油冷具有更多的一次γ′含量和较少的晶界γ′含量。因此,采用300℃盐浴等温可明显改善合金的持久性能。
In this paper, the quantitative metallurgical method was used to determine the quantitative relationship between solid solution temperature, cooling rate and γ ’precipitated phase content and size distribution, which provided the basis for determining the heat treatment process. The results show that the solution temperature increases, γ ’precipitation increased, and peaked at 1120 ℃; beyond this temperature γ’ content decreased. 300 ℃ salt bath isotherm has more γ ’content and less grain boundary γ’ content than water-cooled and oil-cooled. Therefore, the use of 300 ℃ salt bath isothermal can significantly improve the durability of the alloy.
其他文献
从10月19日全球性股票骤然暴跌以来,西方主要金融市场至今仍在起伏动荡。股市行情变幻莫测。此次剧烈震荡是资本主义世界各种可测的和难测的因素综合作用的结果。人们正透过
The most supreme characteristic of SoC (system on chip) era is the high complexity of the chips; architecture and software design have become the indivisible pa
目的:来源于US28受体N末端的诱惑配体多肽H9,以阐明H9的体外活性及其对细胞表面趋化因子受体CX3CR1内化及调变研究,探讨H9对人趋化因子受体CX3CR1的作用及影响。方法:立足US2
日前,杭州摩托罗拉与陕西广电网络传媒股份公司签署了统一数字电视平台战略合作协议。根据此协议,双方将共同成立一个联合实验室。该实验室将设计统一的硬件平台和软件方案,
本文以矿相分析方法,阐述了鞍山赤铁矿粉流态化还原焙砂,经不同条件和大气环境下的再氧化试验后,其焙砂的矿物组成和显微结构特征。从而分析再氧化前后的物相变化情况,以探索
“嘿,我知道你们知道我的外号叫做‘密西西比的子弹’可请别用那俗不可耐的‘让子弹飞’来形容我吧,我早已经是这个联盟里数一数二的球员了,你们可以叫我蒙塔·埃利斯,或者‘
请下载后查看，本文暂不支持在线获取查看简介。
Please download to view, this article does not support online access to view profile.
瓶阀主要零件阀体系采用直径38毫米的HPb59—1铅黄铜棒料,加热后模锻成形,其坯料是3～4米的长棒料经铣切下料而成,这种工艺材料利用率很低。我们经过多次改进设计,研制了黄铜
自1986年底起,日本经济开始呈现景气,1987年的GNP增长率达到3.96%。1987年日本经济呈现景气主要有四个方面的原因。第一,个人消费增加和房产投资活跃。日元升值、石油和其他
总算给猫咪洗了澡,怎么把猫咪弄干却成了大问题,因为一不小心就会让它着凉。洗澡过程中那个无论如何也不能省略的步骤是什么——就是一定要把猫咪擦干。
Finally gave the c