Interfacial reaction product and mechanical properties of the electron beam brazed K465 Ni-based sup
Ni-based superalloy K465 is brazed with BNi-2 filler metal by vacuum electron beam brazing (VEBB). In process of VEBB, e......
Gas pore is a common defect in brazed joint.It lowers the brazing rate and affects the properties of joint.Experimental ......
Wetting of molten cerium on typical carbon materials (graphite, CVD-diamond and NWCNT) and molten Cu
A series of experiments were conducted to investigate the wettability of graphite plate, graphite paper, NWCNTs Buckypap......
研究钎焊连接微型多端口铝管和AA4343/AA3003/AA4343翅片,模拟汽车热交换器核心的微型组件,并优化钎焊条件.考虑5种工艺参数,用Tag......
The wetting behavior of liquid metals is of great importance for many processes.For brazing,however,a targeted modificat......
Nano-Al2O3 particles modified AgCuNi filler was adopted to braze the SiO2 ceramic and TC4. The effects of filler size as......
以WCo75钎料为研究基础,结合分析Co-Nb和Nb-W二元相图,设计了理论成分比例为Co∶W∶Nb=65∶25∶10(%,质量分数)的合金钎料,以期获......
采用72Ag-28Cu钎料对铪与铜进行了真空钎焊试验,钎焊温度为820~920℃,保温时间为1~45 min。研究了钎焊温度与保温时间对Hf/72Ag-28......
Effects of Al2O3 Particulates on the Thickness of Reaction Layer of Al2O3 Joints Brazed with Al2O3-P
该文从挂篮荷载计算、施工流程、支座及临时固结施工、挂篮安装及试验、合拢段施工、模板制作安装、钢筋安装、混凝土的浇筑及养生......
该文从挂篮荷载计算、施工流程、支座及临时固结施工、挂篮安装及试验、合拢段施工、模板制作安装、钢筋安装、混凝土的浇筑及养生......
Al-6.5Si-42Zn and Al-6.5Si-42Zn-0.09Sr filler metals were used for brazing 6061 aluminum alloy. Air cooling and water co......
Cerium and titanium were added to an Al–42Zn–6.5Si brazing alloy, and the subsequent microstructures of the brazing al......
A Ti-Zr-Cu-Ni-Co-Fe-Al-Sn amorphous filler metal for improving the strength of Ti-6Al-4V alloy brazi
Ti50Zr27Cu8Ni4Co3Fe2Al3Sn3 (at%) amorphous filler metal with low Cu and Ni contents in a melt-spun ribbon form was devel......
Microstructure and mechanical properties of the SiC/Zr4 joints brazed with TiZrNiCu filler for nucle
SiC ceramic has been successfully joined to Zr4 alloy using TiZrNiCu filler within the temperature range 1173 K-1263 K a......
The brazing of TiC cermet to iron was carried out at 1223K for 5-20min using Ag-Cu-Zn filler metal. The formation phase......
Microstructures and properties of low-melting-point Al-Cu-Si filler metals prepared by different tec
The Al25Cu6. 5Si0. 09RE (RE = La and Ce) and Al25Cu10.5Si2Ni filler metals were prepared by common metal mold casting, c......
试验选用在制冷行业有着广泛应用的铝铜管接头进行工艺研究,针对钎焊时插接长度分别为3、5、7 mm的铝铜管接头进行了力学性能、气......
Vacuum brazing of TiAl alloy to 40Cr steel was carried out in a vacuum furnace using Ti40Zr10Cu34.95Ni11.2Sn3.85,Ti51Zr8......
针对铜合金馈线波导器件工艺过程中出现的电镀发黑、镀层不牢等难题,进行了大量工艺试验及低温钎焊工艺的优化研究。结果表明,镀层......
Effects of Al2O3 Particulates on the Thickness of Reaction Layer of Al2O3 Joints Brazed with Al2O3-P
In order to understand the rate-controlling process for the interfacial layer growth of brazing joints brazed with activ......
The brazing of 55% SiCp/A356 (volume fraction) composites in air using Zn-Al alloy as a filler metal was investigated. D......
Formation of interfacial brittle phases sigma phase and IMC in hybrid titanium-to-stainless steel jo
The microstructures of the brazed joints for commercially pure Ti and stainless steel were investigated by the applicati......
对低温下采用Zn-5Al钎料超声辅助钎焊2024铝合金进行研究.在温度为400℃时,采用功率为200 W、振幅为15μm、频率为21 kHz的超声对......
为了改善常用钎料对铝基复合材料的润湿性,制备了新型Al- 12Si-xTi系三元活性钎科.研究表明,所添加的Ti以Ti(Al1-xSix)3(0≤x≤0.1......
The effects of Cu foil and Ni foil on the mechanical properties of YG8 hard carbide/4OCr steel brazed joints were invest......
Si/ SiC ceramic composite and Invar alloy were successfully joined by vacuum brazing using Ti50Cu-W filler metals into w......
The effects of Cu,Si,Ni and RE elements (RE=La and Ce) on the melting temperature of Al-Si filler metals were studied by......