The distribution of He in η-Fe_2C has been studied by first-principles calculations.The formation energies of interstitial He and substitutional He(replacing Fe) are 3.76 eV and 3.49 eV,respectively,which are remarkably smaller than those in bcc Fe,indicating that He is more soluble in η-Fe_2C than in bcc Fe.The binding potencies of both a substitutionalinterstitial He pair(1.28 eV) and a substitutional-substitutional He pair(0.76 eV) are significantly weaker than those in bcc Fe.The binding energy between the two He atoms in an interstitial-interstitial He pair(0.31 eV) is the same as that in bcc Fe,but the diffusion barrier of interstitial He(0.35 eV) is much larger than that in bcc Fe,suggesting that it is more difficult for the interstitial He atom to agglomerate in η-Fe_2C than in bcc Fe.Thus,self-trapping of He in η-Fe_2C is less powerful than that in bcc Fe.As a consequence,small and dense η-Fe_2C particles in ferritic steels might serve as scattered trapping centers for He,slow down He bubble growth at the initial stage,and make the steel more swelling resistant.
The distribution of He in η-Fe_2C has been studied by first-principles calculations. The formation energies of interstitial He and substitutional He (replacing Fe) are 3.76 eV and 3.49 eV, respectively, which are remarkably smaller than those in bcc Fe, indicating that He is more soluble in η-Fe_2C than in bcc Fe. The binding potencies of both a substitutional in intein-human He pair (1.28 eV) and a substitutional-substitutional He pair (0.76 eV) are significantly weaker than those in bcc Fe. The binding energy between the two He atoms in an interstitial-interstitial He pair (0.31 eV) is the same as that in bcc Fe, but the diffusion barrier of interstitial He (0.35 eV) is much larger than that in bcc Fe, suggesting that it is more difficult for the interstitial He atom to agglomerate in η-Fe_2C than in bcc Fe.Thus, self-trapping of He in η-Fe_2C is less powerful than that in bcc Fe.As a consequence, small and dense η-Fe_2C particles in ferritic steels might serve as scattered trapping centers for He , slow down He bubble growth at the initial stage, and make the steel more likely resistant.